X12Ni5 European standard cryogenic container plate, X12Ni5 steel plate fixed rolling, X12Ni5 corresp

X12Ni5 European standard cryogenic container plate, X12Ni5 steel plate fixed rolling, X12Ni5 corresp

X12Ni5 European standard cryogenic container plate, X12Ni5 steel plate fixed rolling, X12Ni5 corresponding material

X12Ni5 belongs to the European standard low-temperature nickel alloy steel plate for pressure vessels, and implements the EN10028 standard. X12Ni5 steel plate in the state of normalizing, normalizing + tempering, quenching and tempering.

X12Ni5 steel plate fixed rolling: Wugang Xiangyang

X12Ni5 is mainly used in the construction of cryogenic LNG storage tanks and belongs to low-temperature steel. A low-carbon quenched and tempered steel, martensitic plus bainite

Other grades of the same series

The steel plate X12Ni5 for cryogenic pressure vessel implements the GB245-2009 standard, the size, shape, weight and allowable deviation of X12Ni5 steel plate shall comply with the provisions of GB/T709-2006, its thickness allowable deviation shall comply with the provisions of GB/T709-2006 Class B deviation, and the packaging, marking and quality certificate of steel plate shall comply with the provisions of GB/T247.

S355J2C+N S355K2+N S355NH S355NL S355J2H S355NLH S355G10+N S355G10+M S355G8+N S355G8+M S355MLO S355NLO S460G2+M S460MLO S700MC S690QL S690QL1 S690QLO Dillimax690 Naxtra700 N-a-xtra XABO890 Xabo Dillimax890T X120Mn12 Creusabro8000 Creusabro M Creusabro4800 Creusabro Dual RAEX400 abrazo Aldur700 Aldur Durostat Brinar Alform Dillimax Dillidur Maxil Supralsim

13CrMo4-5 10CrMo9-10 13CrMoV9-10 42CrMo4 16Mo3 P460NH P460NL P460NL1 P460NL2 P355NL P355NL1 P355NL2 P355NH P355GH P235GH TC1 P265GH P295GH SA516GR60 SA516GR70 SA387GR5CL2 SA387GR11CL2 A387GR91 DH36 FH36 VL E36 GL F36 X8Ni9 X12Ni5 X7Ni9 ST52-3 20MnCr5 16MnCr5 C60 S460ML S460NL SIDUR 3401 WearTuf SIQUAL SITHERM SINOXX SIPREME SIMAXX SICLAD SIWATT OCEANFIT DICREST Toughcore API 5L X70

With the increase of tempering temperature, the content of reversed austenite in the steel increases, the low-temperature impact toughness increases, and the matrix structure is purified, and the strength first increases and then decreases. When tempered at 580 °C, with the decrease of holding time, the strength of the steel increases, the plasticity and toughness decrease, and the plasticity is lower than the standard value; The tempering process of QLT heat treatment is 580°C×60min. With the increase of tempering temperature, the content of reversed austenite in the steel increases, the low-temperature impact toughness increases, and the matrix structure is purified, and the strength first increases and then decreases. When tempered at 580 °C, with the decrease of holding time, the strength of the steel increases, the plasticity and toughness decrease, and the plasticity is lower than the standard value; The tempering process of QLT heat treatment is 580°C×60min