CCS-EH36 is a ship plate of China Classification Society, CCS-EH36 ship plate introduction: A, D, E, F is the quality grade, E stands for -40 degree impact, H is the high-strength building materials, 36 maximum compressive resistance, Z is the Z tensile, EH36-Z35.

Chemical composition of CCSEH36 ship plate fixed rolling # Wugang Xiangyang

CCS-EH36 marine steel plate:

carbon C content: ≤0.18, silicon Si content: ≤0.50,

Manganese Mn content: 0.90-1.60, phosphorus P content: ≤0.025

sulfur S content: ≤0.025, copper Cu content: ≤0.35,

chromium Cr content: ≤0.20, nickel Ni content: ≤0.40,

Molybdenum Mo content: ≤0.08, niobium Nb content: 0.02-0.05,

vanadium V content: 0.50-0.10, titanium Ti content: ≤0.02, N:

CCSEH36 marine steel plate specifications:

CCSEH36 steel plate; 20*2200*11000 Ship plate

CCSEH36 steel plate; 30*2200*11000 Ship plate

CCSEH36 steel plate; 35*2200*11000 ship plate

CCSEH36 steel plate; 40*2200*11000 Ship plate

CCSEH36 steel plate; 50*2200*11000 Ship Plate

CCSEH36 Steel Plate; 60*2200*11000 Ship plate

CCSEH36 steel plate; 70*2200*11000 ship plate

CCSEH36 steel plate; 80*2200*11000 ship plate

CCSEH36 steel plate; 90*2200*11000 Ship plate

CCSEH36 steel plate; 100*2200*11000 Ship plate

CCS-EH36 steel plate Z-direction performance:

The Z-direction performance of the steel plate is the thickness direction performance of the steel plate, and it is also the commonly used anti-layered tear steel, and the Z-direction performance steel is often used in the thickness direction of the stressed parts, and the parts that bear high load and high vibration for a long time, so the Z-direction performance steel plate has extremely high requirements for the harmful elements in the steel plate. Z15 requires the sulfur content of the steel plate to be controlled below 0.010 percent, the average elongation after breaking for the three steel plates shall not be less than 15 percent, the elongation of a single sample after breaking shall not be less than 10 percent, Z25 requires the sulfur content to be controlled below 0.007 percent, the average elongation after breaking shall not be less than 25 percent, the average elongation of a single sample shall not be less than 15 percent, Z35 requires the sulfur content to be less than 0.005 percent, the average elongation of the steel plate after breaking is not less than 35 percent, and the single sample is not less than 25 percent